Compoziție chimică
| Compoziție chimică % | ||||||||||
| Si | Fe | Cu | Mn | Mg | Cr | V | Zn | De | Residuals | |
| 6005 | 0.6-0.9 | ≤0.35 | ≤0.10 | ≤0.10 | 0.4-0.6 | ≤0.10 | / | ≤0.10 | ≤0.10 | ≤0.15 |
Mechanical Properties
| Mechanical Properties | |
| Property | Value |
| Elastic (Young’s, Tensile) Modulus | 69 GPa |
| Elongation at Break | 1.1 – 32% |
| Fatigue Strength | 32-71 MPa |
| Shear Modulus | 26 GPa |
Thermal Properties
| Thermal Properties | |
| Property | Value |
| Latent Heat of Fusion | 400 J/g |
| Maximun Temperature | 180 ℃ |
| Melting Completion (Liduidus) | 660 ℃ |
| Thermal Conductivity | 220W/m.K |
| Thermal Expansion | 24 µm/m-K |
Aplicație:
- Manufature of railroad tank cars
- Chemical Equipment
Common Caculations
| Common Calculations | |
| Resilience:Ultimate | 0.76-52 MJ/m³ |
| Resilicence: Unit (Modulus of Resilience) | 5.7-170 KJ/m³ |
| Stiffness to Weight:Bending | 50 points |
| Stiffness to Weight:Axial | 14 points |
| Strength to Weight:Bending | 16-25 points |
| Strengthto Weight:Axial | 8.7-17 points |
| Thermal Diffusivity | 90 mm²/s |
| Thermal Shock Resitance | 3.7-7.4 points |
Variations
1.1100-H112 Aluminum
1100-H112 is 1100 aluminum in the H112 temper. This temper is actually just a variation on F (as-fabricated) that allows for the possibility of very limited strain hardening or heat treatment, under certain conditions.
It has the second lowest strength and second highest ductility compared to the other variants of 1100 aluminiu.
2.1100-H113 Aluminum
1100-H113 is 1100 aluminum in the H113 temper. This temper is a very specific variation on H112 that only applies to standard tube products.
It has the lowest strength compared to the other variants of 1100 aluminiu.
3.1100-H12 Aluminum
1100-H12 aluminum is 1100 aluminum in the H12 temper. To achieve this temper, this metal is strain hardened to a strength that is roughly a quarter of the way between annealed(O) and full -hard (H18).
4.1100-H14 Aluminum
1100-H14 aluminum is 1100 aluminum in the H14 temper. To achieve this temper, this metal is strain hardened to a strength that is roughly a quarter of the way between annealed(O) and full -hard (H18).
5.1100-H16 Aluminum
1100-H16 aluminum is 1100 aluminum in the H16 temper. To achieve this temper, this metal is strain hardened to a strength that is roughly 3/4 of the way between annealed(O) and full -hard (H18).
6.1100-H18 Aluminum
1100-H18 aluminum is 1100 aluminum in the H18 temper. This is the strongest temper normally produced through the action of only strain hardening.
7.1100-H22 Aluminum
1100-H22 aluminum is 1100 aluminum in the H22 temper. To achieve this temper, this metal is strain hardened,and then partially annealed, to a strength that is roughly a quarter of the way between annealed(O) and full -hard (H28).
8.1100-H24 Aluminum
1100-H24 aluminum is 1100 aluminum in the H24 temper. To achieve this temper, this metal is strain hardened,and then partially annealed, to a strength that is roughly halfway between annealed(O) and full -hard (H28).
9.1100-H26 Aluminum
1100-H26 aluminum is 1100 aluminum in the H26 temper. To achieve this temper, this metal is strain hardened,and then partially annealed, to a strength that is roughly 3/4 of the way between annealed(O) and full -hard (H28).
It has the second lowest ductility compared to the other variants of 1100 aluminiu.
10.1100-H28 Aluminum
1100-H28 aluminum is 1100 aluminum in the H 28 temper. This is the strongest temper normally produced through the action of strain hardening followed by partial annealing. It is closely related to related H18. It has the lowest ductility compared to the other variants of 1100 aluminiu.
11.1100-O Aluminum
1100-O aluminum is 1100 aluminum in the annealed condition. It has the highest ductility compared to the other variants of 1100 aluminiu.
Process Flow
FAQ
1. Q:Sunteți producător sau companie comercială?
O: Suntem producator, poate face OEM și ODM.
2. Q: Pot să iau câteva mostre? Ce informații despre produs trebuie să ofer?
O: Da, avem mostre mici, ca dimensiune A4. Trebuie să furnizați nota (NUMĂR ALIE) si temperamentul, grosime, lăţime,lungimea si cantitatea.
3. Q: Cum se descurcă fabrica dumneavoastră în ceea ce privește controlul calității?
O: Calitatea este prioritară. Fabrica noastră a obținut autentificarea SGS. Garantăm mărfurile din fabrica noastră 100% calificat. Și fiecare proces, avem o operare foarte strictă și aranjam 2 tehnicieni să inspecteze. După ce produsele sunt terminate, vom face ultimul test pentru a ridica produsele necalificate.
4. Q：Care este plata ta?
O: În general, acceptăm 30% T/T ca depozit și 70% contra cu copie B/L
Ambalare & Transport