アルミ板 7075 is a high-strength aluminum-zinc (Al-Zn-Mg-Cu) alloy from the 7000 シリーズ, one of the strongest aluminum alloys commercially available. With zinc and magnesium as principal alloying elements and copper for additional strength, 7075 achieves tensile strength comparable to many steels while weighing only one-third as much. It is solution heat treated and artificially aged to T6 or T651 temper for maximum strength. 私たちの 7075 aluminum plates are manufactured per ASTM B209, ギガバイト/トン 3880, AMS 4045, and QQ-A-250/12, widely used in aerospace, defense, tooling, and high-performance structural applications.
化学組成 (%), ギガバイト/トン 3190 & ASTM B209
アル (アルミニウム): 87.1 – 91.4 (バランス)
亜鉛 (亜鉛): 5.1 – 6.1 (主要な合金元素)
マグネシウム (マグネシウム): 2.1 – 2.9
銅 (銅): 1.2 – 2.0
Cr (クロム): 0.18 – 0.28
鉄 (鉄): 0.5 最大
と (シリコン): 0.4 最大
ん (マンガン): 0.3 最大
の (チタン): 0.2 最大
ジル (Zirconium): 0.25 最大 (for 7075-T73 variants)
その他各: 0.05 最大, その他合計: 0.15 最大
機械的性質 (代表的な値)
Temper T6 (Solution Heat Treated & Artificially Aged): 抗張力 510-570 MPa, 降伏強さ 430-505 MPa, 伸長 8-11%
Temper T651 (T6 + Stress Relieved): 抗張力 510-570 MPa, 降伏強さ 430-505 MPa, 伸長 8-11%
Temper T7351 (Overaged + Stress Relieved): 抗張力 460-510 MPa, 降伏強さ 370-430 MPa, 伸長 8-12% (improved SCC resistance)
硬度: 150-160 HB (T6/T651)
疲労強度: 160 MPa (T6, 5×10⁸サイクルで)
剪断強度: 330 MPa (T6)
弾性率: 71.7 GPa (10,400 クシ)
Specific Strength: One of the highest strength-to-weight ratios of any metal alloy
物理的特性
密度: 2.81 g/cm3 (0.1015 ポンド/インチ3)
融点: 477-635℃ (890-1175°F)
熱伝導率: 130 付き(m・K) 25℃で (T6)
電気伝導性: 32% IACS (T6)
電気抵抗率: 5.2 ×10⁻⁸Ω・m
熱膨張係数: 23.6 × 10⁻⁶/K (20-100℃)
弾性率: 71.7 GPa (10,400 クシ)
Poisson Ratio: 0.33
Fatigue Endurance Limit: 160 MPa (T6)
仕様
規格: ASTM B209, ギガバイト/トン 3880, ギガバイト/トン 3190, AMS 4045, QQ-A-250/12, で 485, HE H4000
厚さ: 0.5 んん – 250 んん (0.02″ – 10″)
幅: 500 んん – 2600 んん (カスタムスリットが利用可能)
長さ: 500 んん – 12000 んん (カスタムカットが可能)
気性: ○, T6, T651, T7351, T7451
表面仕上げ: ミル仕上げ, 明るい, Clad (Alclad 7075), Anodized, コーティングされた
許容範囲: 厚さ: ±0.05mm (薄い) to ±0.5mm (厚い), 幅/長さ: ±1mm, Flatness: per ASTM B209
角: せん断エッジ, 鋸で切ったエッジ, または要件に従って
Special: Alclad 7075 利用可能 (with pure aluminum cladding for improved corrosion resistance)
主な特長 & 利点
- Extremely high strength – tensile strength up to 570 MPa, comparable to structural steel
- Outstanding strength-to-weight ratio – the benchmark for aerospace structural alloys
- Heat treatable – T6/T651 temper provides maximum mechanical properties
- 優れた耐疲労性 – excellent for cyclic loading applications
- Excellent machinability in T6 condition – ideal for precision machining
- Good response to anodizing – hard anodizing for wear resistance
- Alclad option available for enhanced corrosion protection
- Consistent properties – solution heat treated, stress relieved, and artificially aged
- Proven performance – the most widely used alloy in aerospace structures
- Readily available in plate form with full traceability documentation
アプリケーション
- 航空宇宙 – aircraft structural components, fuselage frames, wing spars, bulkheads
- 航空宇宙 – helicopter rotors, ミサイル部品, satellite structures
- Defense and military – armor plates, weapons systems, vehicle components
- Tooling and molds – injection molds, blow molds, mold bases, jigs and fixtures
- Precision machinery – 歯車, シャフト, valve components, 高応力部品
- Automotive racing – suspension components, シャーシ部品, drive shafts
- Sports equipment – high-performance bicycle frames, climbing equipment
- Marine engineering – high-strength structures (with protective coating)
- エレクトロニクス – high-strength enclosures, structural frames
- General engineering – high-strength structural applications where weight matters
品質管理 & テスト
私たちのすべてのバッチ 7075 アルミニウム板は厳格な品質管理を受けています:
化学分析: Spectrometer verification of Zn, マグネシウム, 銅, Cr content
Heat Treatment Verification: Conductivity testing, hardness testing to verify T6/T651 treatment
機械試験: 引張試験, 降伏強度試験, elongation test per temper
腐食試験: Stress corrosion cracking (SCC) test per ASTM G47, exfoliation corrosion test per ASTM G34
Ultrasonic Testing: UT inspection per AMS 2630 for aerospace applications
表面検査: 傷の目視検査, 穴, and defects
平坦度チェック: Flatness tolerance per ASTM B209 / ギガバイト/トン 3880
ドキュメンテーション: ミルテスト証明書 (MTC), heat treatment records, 材料のトレーサビリティ, 適合証明書
包装 & 運送
包装: 標準的な輸出梱包 – プレートの間に保護紙を挟んで重ねたプレート, 防水クラフト紙とプラスチックフィルムで包まれています, 木製パレットまたは木箱, スチールストラップ, コーナープロテクション; protective film on request
マーキング: 合金, 気性, サイズ, 熱数, 標準, メーカーロゴ
貿易条件: FOB, CIF, CFR, EXW, DDP
支払い: T/T (30% デポジット, 70% 出荷前に), 一目でわかるL/C, ウエスタンユニオン, ペイパル (サンプル注文)
リードタイム: 標準サイズの在庫あり – 3-7 日々; カスタムサイズ – 15-30 日々
MOQ: 500 標準サイズの場合 kg; カスタムオーダー交渉可能
積み込み口: 青島, 上海, 天津, 寧波, またはリクエストに応じて
私たちを選ぶ理由
以上で 15 アルミニウムの製造と輸出における長年の経験, 私たちは信頼できるサプライヤーです 7075 aluminum plates to aerospace, defense, and precision engineering companies in more than 50 国. 私たちの工場には高度な圧延装置が装備されています, heat treatment, and testing lines, ensuring aerospace-grade quality and consistency. 当社は標準サイズと温度の大量の在庫を維持しており、即時納品が可能です, and our experienced team can provide technical consultation, material certification support, and customized solutions for your specific applications. 競争力のある見積もりについては今すぐお問い合わせください!